- Arts & Culture 6206
- Business & Economics 672
- Computers 316
- Dictionaries & Encyclopedias 71
- Education & Science 76828
- Abstracts 73
- Astrology 4
- Biology 8
- Chemistry 4010
- Coursework 15549
- Culture 8
- Diplomas 316
- Drawings 1596
- Ecology 5
- Economy 76
- English 80
- Ethics, Aesthetics 3
- For Education Students 17562
- Foreign Languages 11
- Geography 3
- Geology 1
- History 88
- Maps & Atlases 5
- Mathematics 12624
- Musical Literature 2
- Pedagogics 19
- Philosophy 22
- Physics 15120
- Political Science 5
- Practical Work 59
- Psychology 63
- Religion 4
- Russian and culture of speech 8
- School Textbooks 7
- Sociology 9
- Summaries, Cribs 87
- Test Answers 160
- Tests 8747
- Textbooks for Colleges and Universities 32
- Theses 7
- To Help Graduate Students 14
- To Help the Entrant 38
- Vetting 382
- Works 13
- Информатика 8
- Engineering 894
- Fiction 706
- House, Family & Entertainment 84
- Law 128
- Website Promotion 68
3. The content of samarium in cerium dioxide was determ
Refunds: 0
Uploaded: 06.03.2021
Content: САМАРИЙ.rar 20,63 kB
Product description
3. The content of samarium in cerium dioxide was determined by the addition method. A standard solution of samarium nitrate was prepared by dissolving 115.8 mg of Sm2O3 in nitric acid. The dry residue after evaporation was dissolved in water and diluted to 100.0 ml (solution A). Then 0.10 ml of solution A was diluted with water to 100.0 ml (solution B).
A sample of СеО2 weighing t mg was mixed with sodium sulfate and divided into two equal parts. One of them was injected with 0.5 ml of solution B; the mixture was dried and calcined. The luminescence intensity of the obtained phosphors (peak height, mm) turned out to be:
Option 1 2 3
m, mg 200 170 190
h, mm 50 40 30
hx + 3, mm. 70 60 55
Calculate the mass fraction (%) of samarium in cerium dioxide.
Additional information
If you do not open the file - install the RAR archiver. Inside the archive you will find a solution in Word format.
Feedback
0| Period | |||
| 1 month | 3 months | 12 months | |
| 0 | 0 | 0 | |
| 0 | 0 | 0 | |